FIRE PROTECTION
SEALXPERT FLAMECEASE FC100 FIRE PROTECTION COATING
FEATURES:
- Low installation cost
- High Durability Fire Tested under British Standard 476 Part 6, 7 & 20
- Contains no halogenated flame retardant
- Excellent lap shear, tensile, and compressive strength
- More specific to address complex issues with different resin types
APPLICATION:
- Ideal for use in:
- Petrochemical plants
- Chemical processing plants
- Gas processing facilities
- Refinery facilities
- Pipe rack beams and columns
- Vessel skirts and supports
- Tank saddles
- Silo top
- Automotive/aircraft parts
- Suitable for both interior and exterior applications
- Suitable for onsite and offsite application
- Apply by using brush or paint roller
- Can be used as primer, fire protection coat and top coat, 3-in-1
- May apply any epoxy base paint coating after FC100 base on personal preferences for aesthetic purpose
TECHNICAL DATA:
| Gel time | : | 15 min |
| Gel to peak exotherm | : | 18 min |
| Total time to peak exotherm | : | 28 min |
| Peak exotherm temperature | : | 174°C (345 °F) |
| Barcol hardness | : | 49 |
| Tensile strength | : | 6672 psi (469 kg/cm 2) |
| Tensile modulus | : | 73 x 10 9 pa |
| Heat distortion temperature | : | 117°C (243 °F)@ 264 psi (19 kg/cm 2) |
| Adhesive strength | : | 1958 psi (138 kg/cm 2) |
| Tensile elongation | : | 2.8% |
| Flexural strength | : | 23931 psi (1683 kg/cm 2) |
| Flexural modulus | : | 6.8 x 10 9 pa |
| Fire Resistance | Recommended Coating Thickness (I-Beam) | Product Usage Per Coating |
|---|---|---|
| 1 hour fire protection |
1.0 mm thk / 2 coatings | 800 grams / m 2 |
| 2 hours fire protection | 1.5 mm thk / 3 coatings | 800 grams / m 2 |
| 3 hours fire protection | 3.5 mm thk / 7 coatings | 800 grams / m 2 |
SEALXPERT FLAMECEASE FC100 FIRE PROTECTION COATING
PACKAGE:
- FC100 Resin (20kg)
- FC100 Hardener (1kg)